Estudo experimental do reforço à flexão em vigas de concreto armado com balanço utilizando compósitos com tecidos de fibras de carbono / Ana Carolina Neves de Araújo, Emil Sánchez, Marta de Souza Lima Velasco
|
| Autores: |
|
| En: |
REVISTA INTERNACIONAL DE DESASTRES NATURALES, ACCIDENTES E INFRAESTRUCTURA CIVIL, vol. 4, núm. 1; mayo 2004: p 11-25. bibl. il. gráf. tablas.
|
| Temas: |
|
| Otros Títulos: |
|
| URL: |
|
| Revista: |
Revista internacional de desastres naturales, accidentes e infraestructura civil, vol. 4, núm. 1; mayo 2004.
|
| Resumen: |
This article presents an experimental study on the flexural behavior of reinforced concrete beams strengthened with externally-bonded carbon fiber polymers. The experimental program consists of the manufacture and tests of seven simple supported R/C beams with one cantilever. The beams have the same cross-section, length, and internal steel reinforcement. The beams were designed in a way that the mid-span bending moment is the same as the cantilever bending moment. The concrete mix was designed for achieving a compressive strength of 20 MPa, and the applied steel reinforcement had a specified yield stress of 500 MPa. A reference beam was tested without the bonded reinforcement. The six strengthened beams were preloaded and the carbon fiber polymer applied under constant deformation. Three beams were equally strengthened in the regions that correspond to the maximum bending moments. In relation to these three first beams, the other three had the strengthening cross-section area duplicated in the region of the maximum negative moment, keeping the same strengthened cross-section area in the region of the positive moment. The structural behavior of these beams was evaluated in terms of deflection, straining of the steel reinforcement, cracking, failure type and failure load. The analysis showed an increase in the strength and the stiffness of the beams, and also that the strengthened technique is efficient and easy to accomplish.
|
| Resumen: |
Esse trabalho apresenta um estudo sobre o comportamento e o desempenho de vigas de concreto armado reforçadas à flexão utilizando-se compósitos de fibra de carbono. O programa experimental constituído pelo ensaio de sete vigas biapoiadas com um vão em balanço, todas com a mesma seção transversal, armaduras de aço e vãos idênticos, sendo o momento positivo máximo igual ao do momento negativo máximo. O concreto utilizado foi projetado para fornecer uma resistência à compressão de 20 MPa e o aço empregado foi o CA-50. Foi ensaiada uma viga de referência sem reforço. As outras seis vigas foram pré-carregadas e reforçadas sob carregamento constante, sendo que três delas foram igualmente reforçadas nas duas regiões de momentos máximos, e as outras três tiveram sua armadura de reforço, em relação às três primeiras, duplicada na região de momento máximo negativo, sendo mantida a área do reforço na região de momento positivo. O comportamento estrutural dessas vigas foi avaliado em termos de flechas, deformação da armadura, fissuração, modo e carga de ruptura. Por meio da análise realizada verificou-se o aumento de resistência e rigidez das vigas reforçadas, constatando-se que o reforço em vigas de concreto armado com compósitos de fibra de carbono é uma técnica eficiente e de fácil execução.
|
| Palabras Claves: |
Palabras claves: vigas de concreto, resistencia de los materiales, conducta de flexión, fibras de carbono.
|
| Areas Temáticas: |
|
|
|
LDR 03979nab a22002175a 4500
001 11158393
003 2009-10-13 22:32:17.0
005 2009-10-13 22:32:17.0
008 051027t2004uuuupr u 0 0 0spa d
030 $aTecnología
040 $aCI
082 $aTecnología
245 00$aEstudo experimental do reforço à flexão em vigas de concreto armado com balanço utilizando compósitos com tecidos de fibras de carbono /$cAna Carolina Neves de Araújo, Emil Sánchez, Marta de Souza Lima Velasco
260 $aREVISTA INTERNACIONAL DE DESASTRES NATURALES, ACCIDENTES E INFRAESTRUCTURA CIVIL,$bvol. 4,$cnúm. 1; mayo 2004: p 11-25. bibl. il. gráf. tablas.
440 0$aRevista internacional de desastres naturales, accidentes e infraestructura civil,$nvol. 4, núm. 1; mayo 2004.
504 $aPalabras claves: vigas de concreto, resistencia de los materiales, conducta de flexión, fibras de carbono.
520 0 $aThis article presents an experimental study on the flexural behavior of reinforced concrete beams strengthened with externally-bonded carbon fiber polymers. The experimental program consists of the manufacture and tests of seven simple supported R/C beams with one cantilever. The beams have the same cross-section, length, and internal steel reinforcement. The beams were designed in a way that the mid-span bending moment is the same as the cantilever bending moment. The concrete mix was designed for achieving a compressive strength of 20 MPa, and the applied steel reinforcement had a specified yield stress of 500 MPa. A reference beam was tested without the bonded reinforcement. The six strengthened beams were preloaded and the carbon fiber polymer applied under constant deformation. Three beams were equally strengthened in the regions that correspond to the maximum bending moments. In relation to these three first beams, the other three had the strengthening cross-section area duplicated in the region of the maximum negative moment, keeping the same strengthened cross-section area in the region of the positive moment. The structural behavior of these beams was evaluated in terms of deflection, straining of the steel reinforcement, cracking, failure type and failure load. The analysis showed an increase in the strength and the stiffness of the beams, and also that the strengthened technique is efficient and easy to accomplish.
520 0 $aEsse trabalho apresenta um estudo sobre o comportamento e o desempenho de vigas de concreto armado reforçadas à flexão utilizando-se compósitos de fibra de carbono. O programa experimental constituído pelo ensaio de sete vigas biapoiadas com um vão em balanço, todas com a mesma seção transversal, armaduras de aço e vãos idênticos, sendo o momento positivo máximo igual ao do momento negativo máximo. O concreto utilizado foi projetado para fornecer uma resistência à compressão de 20 MPa e o aço empregado foi o CA-50. Foi ensaiada uma viga de referência sem reforço. As outras seis vigas foram pré-carregadas e reforçadas sob carregamento constante, sendo que três delas foram igualmente reforçadas nas duas regiões de momentos máximos, e as outras três tiveram sua armadura de reforço, em relação às três primeiras, duplicada na região de momento máximo negativo, sendo mantida a área do reforço na região de momento positivo. O comportamento estrutural dessas vigas foi avaliado em termos de flechas, deformação da armadura, fissuração, modo e carga de ruptura. Por meio da análise realizada verificou-se o aumento de resistência e rigidez das vigas reforçadas, constatando-se que o reforço em vigas de concreto armado com compósitos de fibra de carbono é uma técnica eficiente e de fácil execução.
650 0$aFlexión
650 0$aVigas de hormigón
700 10$aNeves de Araújo, Ana Carolina
740 0 $aExperimental study of R/C beams strengthened in flexure with externally-bonded carbon fiber polymers
856 78$uhttp://academic.uprm.edu/laccei/index.php/RIDNAIC/article/viewFile/73/78
|